| Items |
 JR150R025-NH150 Armtex® Jafrib® 25 ft Available Length, 1 1/2 in. Size, and NST Coupling Type Red Layflat Fire Hose - Assembled Lengths |
JR150R050-NH150 Armtex® Jafrib® 50 ft Available Length, 1 1/2 in. Size, and NST Coupling Type Red Layflat Fire Hose - Assembled Lengths |
JR150R100-NH150 Armtex® Jafrib® 100 ft Available Length, 1 1/2 in. Size, and NST Coupling Type Red Layflat Fire Hose - Assembled Lengths |
JR150R025-NP150 Armtex® Jafrib® 25 ft Available Length, 1 1/2 in. Size, and NPSH Coupling Type Red Layflat Fire Hose - Assembled Lengths |
JR150R050-NP150 Armtex® Jafrib® 50 ft Available Length, 1 1/2 in. Size, and NPSH Coupling Type Red Layflat Fire Hose - Assembled Lengths |
|||||
| General Applications |
|
|||||||||
| Construction | Made from circularly woven 100% high tenacity synthetic yarn, completely protected and locked-in by a tough, highly resistant synthetic nitrile rubber and PVC blend extruded through the weave and forming a single homogenous construction without the use of glues or adhesives. | |||||||||
| Lining Properties | The tensile strength of the lining and cover shall not be less than 1,750 PSI (12,000 kPa), with an ultimate elongation of liner and cover not less than 450%. | |||||||||
| Accelerated Aging | Lining specimens subjected to an exposure of 158 ºF ± 3.6 ºF, for a duration of 96 hours shall be conditioned as per ASTM D 573, Standard Test Method for Rubber - Deterioration in an Air Oven. Then, the specimens shall be tested to ASTM D4112, Standard Test Methods for Vulcanized Rubber and Thermoplastic Elastomers- Tension, Method A. Upon evaluation, the tensile and elongation properties of the liner shall not be less than 75% of their initial values. | |||||||||
| Abrasion Resistance | As stated in National Fire Protection Association (NFPA) 1961, Underwriters Laboratories (UL) 19 and Factory Mutual Approval Standard (FM) 2111, hose shall withstand 1 1/2 times the service test pressure without rupturing or breaking any thread in the jacket or reinforcement after 300 cycles of abrasion for a single jacketed hose. Hose assembly shall also not leak or burst after 3,000 cycles by an abrasion wheel. | |||||||||
| Service Temperature Range [Min] | -30 ºC-22 ºF | |||||||||
| Service Temperature Range [Max] | 80 ºC176 ºF | |||||||||
| Features and Advantages |
|
|||||||||
| Packaging | Available in 25', 50', and 100' lengths. | |||||||||
| Size | 1 1/2 in | |||||||||
| Color | Red | |||||||||
| Coupling Size | 1 1/2 in | |||||||||
| Coupling Type | NST | NST | NST | NPSH | NPSH | |||||
| Bowl Size | 1 3/4 in | |||||||||
| Service Test | 300 psi | |||||||||
| Proof Test | 600 psi | |||||||||
| Burst Test | 900 psi | |||||||||
| Available Lengths | 25 ft | 50 ft | 100 ft | 25 ft | 50 ft | |||||
| Weight Uncoupled | 0.30 lbs/ft | |||||||||
| Brand | Armtex® | |||||||||
| Type | Fire Hose Assembly | |||||||||
| Material | Reinforced Extruded Rubber | |||||||||
| Warranty | 10 y | |||||||||
| Industry Standards | Underwriters Laboratories (UL) 19 and Underwriters Laboratories of Canada (ULC) - S511-14 Certified, International Organization for Standardization (ISO) 9001 | Underwriters Laboratories (UL) 19 and Underwriters Laboratories of Canada (ULC) - S511-14 Certified, Meets or exceeds National Fire Protection Association (NFPA) 1961, International Organization for Standardization (ISO) 9001 | Underwriters Laboratories (UL) 19 and Underwriters Laboratories of Canada (ULC) - S511-14 Certified, Meets or exceeds National Fire Protection Association (NFPA) 1961, International Organization for Standardization (ISO) 9001 | Underwriters Laboratories (UL) 19 and Underwriters Laboratories of Canada (ULC) - S511-14 Certified, Meets or exceeds National Fire Protection Association (NFPA) 1961, International Organization for Standardization (ISO) 9001 | Underwriters Laboratories (UL) 19 and Underwriters Laboratories of Canada (ULC) - S511-14 Certified, Meets or exceeds National Fire Protection Association (NFPA) 1961, International Organization for Standardization (ISO) 9001 | |||||
| Construction | ||||||||||
|
|
||||||||||